Name: ASME SA182 F304H Stainless Steel Ring 1.4948 Steel Forged Ring Heat Exchanger Spare Parts
Brand: Yuhong Group Co.,Ltd
SKU: ASME SA182 F304H Kuty pierścień ze stali nierdzewnej
Price: 150000 USD
Availability: InStock

Yuhong Holding Group Co., LTD

Polish

Dom

Produkty

O nas

Wycieczka po fabryce

Kontrola jakości

Skontaktuj się z nami

Wiadomości Firmowe

Dom Produkty Kołnierz stalowy

ASME SA182 F304H Stainless Steel Ring 1.4948 Steel Forged Ring Heat Exchanger Spare Parts

Szczegóły Produktu:

Miejsce pochodzenia:	Chiny
Nazwa handlowa:	YUHONG
Orzecznictwo:	ASME II, ASME III, ABS, LR, DNV, GL , BV, CCS, KR, NK, TUV, PED, GOST, ISO , TS
Numer modelu:	ASME SA182 F304H Kuty pierścień ze stali nierdzewnej

Zapłata:

Minimalne zamówienie:	1 szt
Szczegóły pakowania:	Drewniana skrzynia / paleta
Czas dostawy:	7 dni
Zasady płatności:	L/C, T/T

Kontakt

Wszystkie produkty

Bezszwowa rura ze stali nierdzewnej (342)

Bezszwowa rura ze stali nierdzewnej (337)

Dwustronna rura ze stali nierdzewnej (134)

Dwustronna rura ze stali nierdzewnej (39)

Rurka igłowa (170)

Fin Tube (735)

Wymiennik ciepła (35)

Rura wymiennika ciepła (474)

Zestaw rur wymiennika ciepła (52)

Arkusz rurowy wymiennika ciepła (128)

wyłącznik wymiennika ciepła (39)

Klimatyzer (14)

Zbiornik ciśnieniowy (4)

Spawana rura ze stali nierdzewnej (61)

Spawana rura ze stali nierdzewnej (134)

Nikiel rur (276)

Rura ze stopu niklu (104)

Rura ze stopu miedzi (258)

Rura ze stali stopowej (219)

Rurka tytanowa (21)

Jasna rura wyżarzana (173)

Rura kotła (155)

okucie stalowe (874)

Kołnierz stalowy (672)

Inni (409)

Elementy okładzin (9)

Szczegółowy opis produktu

Nazwa produktu:	kuty pierścień	Standard:	ASTM A182, ASME SA182
Tworzywo:	304H, 1,4948	Rozmiar:	może niestandardowe, jako wymagania rysunkowe kupującego
Kształt:	Pierścień	Badania NDT:	100% PT, UT, PMI
Aplikacja:	Wymiennik ciepła, kocioł, zbiornik ciśnieniowy, turbina parowa, duża centralna klimatyzacja itp.
Podkreślić:	ASME SA182 F304H stainless steel ring , 1.4948 steel forged ring , heat exchanger spare parts steel ring

ASME SA182 F304H Stainless Steel Forged Ring for Heat Exchanger Application

ASME SA182 F304H forged ring is a forged austenitic stainless-steel specification for high-temperature heat exchanger structural parts (tubesheets, flanges, channel rings). Grade F304H features a controlled 0.04–0.10% carbon range, giving it significantly higher creep and stress-rupture strength above 540°C compared to standard 304/L grades—critical for long-term operation. Supplied solution-annealed with fine grain size (ASTM 7+), these forged rings undergo ultrasonic and penetrant inspections. They pair excellently with TP321 tubes due to matched thermal expansion but are incompatible with CuNi 70/30 tubes without electrical isolation, as F304H is far more noble in seawater, inducing rapid galvanic corrosion.

Function of Forged Rings in Heat Exchangers

These are the heavy structural components, not the tubes themselves:

Tubesheets: The thick drilled ring/plate that holds the tube bundle (e.g., TP321 tubes). F304H provides the strength to withstand high differential pressure between shell-side and tube-side fluids.
Flange Rings: Welded or integral rings at the channel ends for bolting to piping or bonnets.
Channel Barrels / Closures: Cylindrical forged sections for high-pressure inlet/outlet headers.
Bearing / Support Rings: Internal rings supporting tube bundles or flow distributors.

Chemical composition % of ASME SA182 F304H Stainless Steel Forged Ring Heat Exchanger Spare Parts

Geade	C	Mn	Si	P	S	Cr	Ni	N
304H	min: 18.0 max:20.0	min: 8.0 max: 10.5	min: 0.04 max:0.10	0.75 max	2.0 max	0.04 max	0.03 max	0.10 max

Mechanical properties of grade ASTM A182 F304H Flange are displayed in the following table.

Grade	Tensile Strength (MPa) min	Yield Strength 0.2% Proof (MPa) min	Elongation (% in 50mm) min	Hardness
				Rockwell B (HR B) max	Brinell (HB) max
304H	515	205	40	92	201

Physical properties of ASME SA182 F304H Stainless Steel Forged Ring Heat Exchanger Spare Parts

Grade	Density(kg/m3)	Elastic Modulus (GPa)	Mean Coefficient of Thermal Expansion (μm/m/°C)			Thermal Conductivity (W/m.K)		Specific Heat 0-100°C (J/kg.K)	Electrical Resistivity (nΩ.m)
			0-100°C	0-315°C	0-538°C	at 100°C	at 500°C
304H	8000	193	17.2	17.8	18.4	16.2	21.5	500	720

Specific Requirements for Heat Exchanger Spare Parts (Forged Rings)

When used for tubesheets, flanges, or channel barrels, forged rings must meet these critical requirements:

Grain Size: ASME SA182 requires a fine grain size (ASTM No. 7 or finer) for F304H to meet creep design curves. Coarser grains reduce rupture life.
Ultrasonic Examination (UT): For hollow forgings (rings) over specific thicknesses, UT is required to detect internal laminations or porosity.
Liquid Penetrant Examination (PT): Required for surface defect detection on finished machined surfaces (sealing faces of flanges).
Solution Annealing: Must be heated to 1040°C – 1120°C and rapidly quenched (water or rapid air) to put carbides into solution before service.

Application